Porous agarose/Gd-hydroxyapatite composite bone fillers with promoted osteogenesis and antibacterial activity

Artificial bone fillers are essentially required for repairing bone defects, and developing the fillers with synergistic biocompatibility and anti-bacterial activity persists as one of the critical challenges. In this work, a new agarose/gadolinium-doped hydroxyapatite filler with three-dimensional porous structures was fabricated. For the composite filler, agarose provides three-dimensional skeleton and endows porosity, workability, and high specific surface area, hydroxyapatite (HA) offers the biocompatibility, and the rare earth element gadolinium (Gd) acts as the antibacterial agent. X-ray photoelectron spectroscopy detection showed the doping of Gd in HA lattice with the formation of Gd-HA interstitial solid solution. Attenuated total reflection Fourier transform infrared spectroscopy imaging suggested chemical interactions between agarose and Gd-HA, and the physical structure of agarose was tuned by the Gd-doped HA. Cytotoxicity testing and alizarin red staining experiments using mouse pro-osteoblasts (MC3T3-E1) revealed remarkable bioactivity and osteogenic properties of the composite fillers, and proliferation and growth rates of the cells increased in proportion to Gd content in the composites. Antibacterial testing using the gram-positive bacteria S. aureus and the gram-negative bacteria E. coli indicated promising antibacterial properties of the fillers. Meanwhile, the antibacterial properties of composite filles were enhanced with the increase of Gd content. The antibacterial fillers with porous structure and excellent physicomechanical properties show inspiring potential for bone defect repair.     

Energy,exergy and exergo-environmental impact assessment of a solid oxide fuel cell coupled with absorption chiller & cascaded closed loop ORC for multi-generation

A novel solid oxide fuel cell (SOFC) multigeneration system fueled by biogas derived from agricultural waste (maize silage) is designed and analyzed from the view point of energy and exergy analysis. The system is proposed in order to limit the greenhouse gas emissions as it uses a renewable energy source as a fuel. Electricity, domestic hot water, hydrogen and cooling load are produced simultaneously by the system. The system includes a solid oxide fuel cell; which is the primary mover, a biogas digester subsystem, a cascaded closed loop organic Rankine cycle, a single effect LiBr-water absorption refrigeration cycle, and a proton exchange membrane electrolyzer subsystem. The proposed cascaded closed-loop ORC cycle is considered as one of the advanced heat recovery technologies that significantly improve thermal efficiency of integrated systems. The thermal performance of the proposed system is observed to be higher in comparison to the simple ORC and the recuperated ORC cycles. The integration of a splitter to govern the flue gas separation ratio is also introduced in this study to cater for particular needs/demands. The separation ratio can be used to vary the cooling load or the additional power supplied by the ORC to the system. It is deduced that net electrical power, cooling load, heating capacity of the domestic hot water and total energy and exergy efficiency are 789.7 kW, 317.3 kW, 65.75 kW, 69.86% and 47.4% respectively under integral design conditions. Using a parametric approach, the effects of main parameters on the output of the device are analyzed. Current density is an important parameter for system performance. Increasing the current density leads to increased power produced by the system, decreased exergy efficiency in the system and increased energy efficiency. After-burner, air and fuel heat exchangers are observed to have the highest exergy destruction rates. Lower current density values are desirable for better exergy-based sustainability from the exergetic environmental impact assessment. Higher current density values have negative effect on the environment.     

Hydrangea like composite catalysts of ultrathin Mo2S3 nanosheets assembled on N,S-dual-doped graphitic biocarbon spheres with highly electrocatalytic activity for HER

Water electrolysis is the most clean and high-efficiency technology for production of hydrogen, an ultimate clean energy in future. Highly efficient non-noble electrocatalysts for hydrogen evolution reaction (HER) are desirable for large scale production of hydrogen by water electrolysis. Especially, exposing as many active sites as possible is a vital way to improve activities of the catalysts. Herein, a series of new hydrangea like composite catalysts of ultrathin Mo₂S₃ nanosheets assembled uprightly and interlacedly on N, S-dual-doped graphitic biocarbon spheres were facilely prepared. The unique structure endowed the catalysts highly exposed edge active sites and prominently high activities for HER. Especially, the optimized catalyst Mo₂S₃/NSCS-50 exhibited as low as 106 mV of overpotential at 10 mA/cm² (denoted as ?₁₀). The catalyst also showed low Tafel slope of 53 mV/dec, low electron transfer resistance of 34 Ω and high stability evidenced by the result that the current density only attenuated 11.7% after 10 h i-t test. The catalyst has shown broad prospect for commercial application in water electrolysis.     

Nanofiber structured oxygen defective CoFe2O4-x catalyst for the water-gas shift reaction in waste-to-hydrogen processes

Waste-to-hydrogen processes are a way to produce hydrogen from waste and reduce the amount of landfill/incineration of wastes simultaneously through the gasification of waste. The water-gas shift (WGS) reaction is a key step in this waste-to-hydrogen process by removing the CO and producing additional H₂. A nanofiber-structured CoFe₂O₄ catalyst was synthesized by the electrospinning method, and the catalytic performance in WGS using waste-derived synthesis gas was compared with that of catalysts prepared by sol-gel, hydrothermal, and co-precipitation methods. The CoFe₂O₄ catalyst synthesized by the electrospinning method showed a clear nanofiber structure and revealed a superior redox property. This superior redox property, which has a large relation with the high oxygen storage capacity of the catalyst, induced the formation of an active phase (Co⁰ and Fe₃O₄) in CoFe₂O₄. As a result, the nanofiber structured oxygen defective CoFe₂O_4-x prepared by the electrospinning method showed the best catalytic activity in this study.     

Facile self-assembly approach to construct a novel MXene-decorated nano-sized phase change material emulsion for thermal energy storage

In recent years, phase change material emulsions (PCMEs) with enhanced energy storage capacities and good flow characteristics have drawn significant attention. However, due to the thermodynamically unstable nature and tiny particle confinement, the nanomaterial modification strategies at PCM/water interface to improve stabilities and reduce supercooling of nano-sized PCMEs (NPCMEs) are very limited and challenging. Herein, we report a facile strategy for constructing MXene-decorated NPCME with good stability, little supercooling, and high thermal conductivity by self-assembly of MXene nanosheets at PCM/water interface. The concentrations of MXene have great influences on the average droplet diameters, stabilities, and thermophysical properties of the NPCMEs. The results show that the PCMs have been well dispersed into the water in the form of quasi-spherical droplets, with average droplet diameters of 242–805 nm. The thermal conductivity of 10 wt% n-tetradecane/water NPCME containing 9 mg ml^-1 MXene is 0.693 W m^-1·K^-1, achieving an enhancement by 15.5%, as compared to that of water. Besides, the MXene-decorated paraffin/water NPCMEs exhibit little supercooling and enhanced heat storage capacities. More importantly, this facile self-assembly strategy opens a new platform for preparing high-performance NPCMEs, which can be used as novel heat transfer fluids for thermal energy storage systems.     

Preparation and properties of AZO/PS/AZO tri-layer transparent conductive film with a light-trapping structure

The light-trapping structure is an effective method to increase solar light capture efficiency in the solar cells. In this study, Al-doped ZnO (AZO)/polystyrene (PS)/AZO tri-layer transparent conductive film with light-trapping structure was fabricated by magnetron sputtering and liquid phase methods. The structural, optical and electrical properties of the AZO films could be controlled by different growth conditions. When the sputtering pressure of the under-layer AZO film was 0.2 Pa, the discharge voltage was around 80 V, which was within the optimal process window for obtaining AZO film with high crystallinity. The optimal under-layer AZO film had a large surface roughness and a very low static water contact angle of 75.71°, promoting the relatively uniform distribution of PS spheres. Under this sputtering condition, the prepared AZO/PS/AZO tri-layer film had the highest crystallinity and least point defects. The highest carrier concentration and Hall mobility are 3.0 × 10²¹ cm^-3and 5.39 cm² V^-1 s^-1, respectively. Additionally, a transparent conductive film with the lowest resistivity value (3.88 × 10^-4 Ω cm) and the highest average haze value (26.5%) was obtained by optimizing the process parameters. These properties were comparable to or exceed the reported values of surface-textured SnO₂-based as well as ZnO-based TCOs films, making our films suitable for transparent electrode applications, especially in thin-film solar cells.     

Microstructure and some properties of powder-pack borided Ti–5Mo–5V–8Cr–3Al alloy with special attention to the microstructure at the interface TiB/substrate

The borided layer was prepared on the surface of the Ti–5Mo–5V–8Cr–3Al alloy by powder-pack boriding at 1000°C-10h. SEM, EPMA and TEM were used to investigate the effects of alloying elements (Al, V, Mo and Cr) on the growth of TiB whiskers in the borided Ti–5Mo–5V–8Cr–3Al alloy. Wear properties of borided Ti–5Mo–5V–8Cr–3Al alloy were investigated using dry reciprocating friction tests. SEM results show that the thickness of boride layer in Ti–5Mo–5V–8Cr–3Al alloy is thinner than that in the Cp-Ti. This is attributed to the enrichment of alloying elements especially V in TiB/substrate by TEM, which hinders the diffusion of B atoms, thus resulting in the short and thick TiB whiskers in Ti–5Mo–5V–8Cr–3Al alloy. Borided Ti–5Mo–5V–8Cr–3Al alloy has the better wear resistance than as-received alloy.     

雪菊精油对希氏肠球菌产酪胺及相关基因表达的影响

探讨不同质量浓度雪菊精油对希氏肠球菌（Enterococcus hirae）N47产酪胺的影响机制。利用反转录实时定量聚合酶链式反应分析E. hirae在雪菊精油作用下酪氨酸脱羧途径相关基因的表达情况；利用高效液相色谱法检测不同质量浓度雪菊精油对E. hirae产酪胺的影响。并将E. hirae接入到含不同质量浓度雪菊精油的熏马肠中发酵，评估香肠pH值、菌落总数和酪胺积累量。结果表明：在E. hirae纯培养体系和熏马肠体系中，雪菊精油通过抑制微生物的生长和酪氨酸脱羧途径中tyr DC、tyr P基因的表达，降低酪胺的积累量（P＜0.05）。当雪菊精油添加量为1/2最小抑菌浓度（minimal inhibitory concentration，MIC）和MIC时，熏马肠中酪胺的含量分别为78.52 mg/kg和45.83 mg/kg，较对照组分别减少了64.72%和79.41%。     

基于乙酰胆碱酯酶和氧化应激研究海胆酮对阿尔茨海默症的作用机制

海胆酮是一种酮式类胡萝卜素，主要从海胆及藻类等海洋生物中提取。本文研究海胆酮对乙酰胆碱酯酶（acetylcholinesterase，AChE）的抑制作用，应用酶动力学、荧光光谱、圆二色光谱和分子对接技术研究海胆酮对AChE的抑制机理，并用淀粉样β蛋白片段25～35（amyloid beta-peptide 25-35，Aβ25-35）诱导大鼠肾上腺嗜铬细胞瘤细胞（PC12细胞）建立阿尔茨海默症（Alzheimer’s disease，AD）模型，研究海胆酮对AD细胞模型氧化应激损伤的作用。结果表明，海胆酮有很强的AChE抑制活性，其半抑制质量浓度为（16.29±0.97）μg/mL，抑制常数Ki为3.82 μg/mL，表现为竞争性抑制；海胆酮可诱导AChE二级结构改变，更容易与AChE活性中心氨基酸Ser200、His440、Trp84和Tyr121结合，阻碍底物碘代硫代乙酰胆碱（acetylthiocholine iodide，ATCI）与酶结合，从而引起酶活力降低。海胆酮能有效抑制Aβ25-35诱导PC12细胞的AChE活力，降低丙二醛含量，增加超氧化物歧化酶、过氧化氢酶和谷胱甘肽过氧化物酶活力，减轻Aβ25-35诱导的PC12细胞氧化应激损伤。本研究基于AChE和氧化应激阐明了海胆酮对AD的潜在作用机制，为海胆酮在功能食品、生物医药等领域的应用提供了数据支持和理论根据。